Location: Home > Products > Hot Work Mould Steel > H13 1.2344 SKD61 4Cr5MoSiV1
H13 1.2344 SKD61 4Cr5MoSiV1 Hot Work Tool Steel
Main Product: H13 1.2344 SKD61 4Cr5MoSiV1
| 1.2344 H13 SKD61 4Cr5MoSiV1 Supply Situation | ||
| Flat Bar | Round bar | |
| Thickness/ Dia | 8 – 500mm | 16 – 800mm |
| Surface | Black Surface / Milling or machined surface | Black Surface / Turned surface |
| Delivery Condition | Hot Rolled / Hot Forged ;EAF/ ESR ; Annealed | Hot Rolled / Hot Forged ; EAF/ ESR ; Annealed |
Products
Related Products
1.2344 Flat Bar
SKD61 Round Bar
1.2344 H13 SKD61 4Cr5MoSiV1 Hot Work Tool Steel For Die-Casting Dies
1.2344/SKD61/H13 hot work tool steel is smelted in an electric furnace and electroslag remelted. Steel is purer and tougher. It is suitable for making aluminum, zinc, copper alloy extrusion dies, die-casting dies, hot forging dies, hot shear blades and other small-sized bright steel (peeling, cold drawing) materials. It is an ideal material for making molds.
1.2344/SKD61/H13 hot work tool steel has a very good metallic luster, 1.2344/SKD61/H13 series products include: thimble, guide post, guide sleeve, cylinder, punch, floating pin and other precision high temperature parts.
1.2344 International Standard:
| DIN | JIS | GB | CHINA |
| 1.2344 | SKD61 | H13 | 4Cr5MoSiV1 |
1.2344 Chemical Composition(%):
| C | Si | Mn | P | S | Cr | Mo | V |
| 0.35-0.42 | 0.80-1.20 | 0.25-0.50 | ≤0.030 | ≤0.030 | 4.80-5.50 | 1.10-1.50 | 0.80-1.15 |
1.2344 Available Size(mm) :
| Flat Bar Size(mm) | Round Bar Size(mm) | |||
| Thickness | Width | Length | Diameter | Length |
| 8-500 | 210-610 | 2000-5800 | 16-800 | 2000-5800 |
1.2344 Delivery Condition:
Black Surface / Milling Surface / Turning Surface
Hot Rolled / Forged ；EFA / ESR ; Annealed
1.2344 Delivery Time:
The stock 1.2344 sizes will be delivered within 10-15 days.
The customized, will be about 30-35 days.
1.2344 Product Process:
Electric-Furnace Smelting(EF)→Ladle Furnace(LF)→Vacuum Degassing(VD)→ Argon protected ingot →Multidirectional Forging → (Concave forging →)Normalizing+Hydrogen Diffusion Annealing → Ultrasonic Flaw Detection →Queching+Tempering Prehardened