Location: Home > Products > Cold Work Mould Steel > Cr12MoV
Cr12MoV Cold Work Mould Steel
Main Product: Cr12MoV Flat Bar, Cr12MoV Round Bar
| Cr12MoV SKD11 D2 1.2601 Supply Situation | ||
| Flat Bar | Round bar | |
| Thickness/ Dia | 10 – 200mm | 10 – 700mm |
| Surface | Black Surface / Milling or machined surface | Black Surface / Turning surface |
| Delivery Condition | Hot Rolled / Hot Forged ;EAF/ ESR ; Annealed | Hot Rolled / Hot Forged ; EAF/ ESR ; Annealed |
Products
Related Products
D2 1.2379 SKD11 Cr12Mo1V1
D3 Cr12 SKD1
DC53
O1 1.2510 SKS3 9CrWMn
Cold Work Die Mould Alloy Tool Steel Cr12MoV SKD11 D2 1.2601
Cr12MoV is widely used in China, Vietnam, Thailand, India, etc.. It is the economic grade of Compared with 1.2379, D2 and SKD11, with the lower content of Mo and V..
It’s used for making high-duty cutting tools (dies and punches), blanking and punching tools, wood working tools, shear blades for cutting light-gauge material, thread rolling tools, tools for drawing, deep drawing and cold extrusion, pressing tools for the ceramics and pharmaceutical industries, cold rools (working rolls) for multiple-roll stands, measuring instruments and gauges, small moulds for the plastics industry where excellent wear resistance is required
Cr12MoV SKD11 D2 1.2601 Tool Steel International Standard
| GB | DIN | ASIA | JIS |
| Cr12MoV | 1.2601 | D2 | SKD11 |
Cr12MoV SKD11 D2 1.2601 Tool Alloy Steel Chermical Compisition(Wt%)
| C | Cr | Mn | Mo | Si | V | P | S |
| 1.45-1.7 | 11-12.5 | ≤0.4 | 0.4-0.6 | ≤0.4 | 0.15-0.3 | ≤0.03 | ≤0.03 |
Cr12MoV SKD11 D2 1.2601 Flat Bar Available Size(mm)
| Flat Bar Size | Round Bar Size(mm) | |||
| Thickness | Width | Length | Diameter | Length |
| 10-200 | 155-810 | 2000-6000 | 10-700 | 3000-6000 |
Cr12MoV SKD11 D2 1.2601 Alloy Steel Heat Treatment Condition
High hardness, high wear resistance eutectic carbide is uniform, good toughness, not easy to crack, hardness after quenching> 62HRC. Nitriding treatment time at 525 ºC is 20h / 30h / 60h, depth of ammoniated layer is 0.25mm / 0.30mm / 0.35mm, surface hardness of parts is 1250HV; nitriding treatment time at 570 ºC is 2h, nitride layer depth is 10 ~ 20μm, parts surface hardness 950HV.
Cr12MoV SKD11 D2 1.2601 Flat Bar Round Bar Delivery Condition
Black Surface / Milling Surface / Turning Surface
Hot Rolled / Forged; EFA / ESR; Annealed
Cr12MoV SKD11 D2 1.2601 Tool Steel Delivery Time
Stock: within 10-15 days.
Future goods: 30-35 days.